Aluminium foil/strips: EN AW-5754 / EN AW-Al Mg3 Material EN AW-5754 / EN AW-Al Mg3 according to DIN EN 573-3:2009-08 Article number UWAL 2100 Product group 5754 Material XX Hardness XXXX Thickness XXXXXX Width Material conditions H111 / H22 / H24 semi-hard / O soft (other hardnesses upon request) according to DIN 485-2 or
This data sheet applies to aluminium 5754 hot and cold-rolled sheets, strips and plates, cold drawn and extruded rod/bar, tubes and profiles made of aluminium magnesium alloy EN AW-5754. Application. The material EN AW-5754 shows high mechanical properties among the non-heat treatable aluminium alloys and shows a very good atmospheric and
、、，Al－Mg。. ，5754（、、）、。. . 5754、、
5754 (AlMg3, 3.3535, A95754) Aluminum. 5754 aluminum is a 5000-series aluminum alloy: the main alloying addition is magnesium, and it is formulated for primary forming into wrought products. 5754 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN
SABATER FUNDIMOL pág. (33) ALUMINIOS Aleaciones Aluminio - Magnesio 5754 Propiedades mecánicas Norma: EN 755-2 Aleación: EN AW-5754 [Al Mg3] Barra extruida Estado de Medidas mm R m MPa R p0,2 MPa A % A 50 mm % tratamiento D1) S2) mín. máx. mín. máx. mín mín. F4), H112 ≤ 150 ≤ < D ≤ < S ≤
H,2 0,5 1,5 3 6 12,5 0,5 1,5 3 6 12,5 130 - - - - - 9 7 8 10 - 1,5t 1,5t 2,0t - - - Technisches Datenblatt EN AW-5754 (AlMg3) Stangen: Maße (mm) Zugfestigkeit R m MPa Streckgrenze R p0,2 MPa Bruchdehnung D1 S2 A% A 50mm %
EN AW-5754 (ALMg3). AL-Mg3，，，：，，，，，，，
EN AW-5754, ČSN ,AlMg3. Základní technické informace, mechanické a technologické vlastnosti, příklady aplikace, dostupné výrobky. EN AW-5754 (AlMg3) má výbornou odolnost proti korozi zejména u mořské vody a průmyslově znečištěných
5754：. 1、 σb (MPa)：190～240。. 2、 σb (MPa)：≥80. 3、：≥12. (GB/T 3880-2006)，。. 5754：. 5754、、，Al-Mg
5754 - H22 Sheet and Plate. Aluminium 5754 has excellent corrosion resistance especially to seawater and industrially polluted atmospheres. It has higher strength than 5251. This high strength makes 5754 highly suited to flooring applications. Please note that Mechanical Properties shown are for
Aluminium foil/strips: EN AW-5754 / EN AW-Al Mg3 Material EN AW-5754 / EN AW-Al Mg3 according to DIN EN 573-3:2009-08 Article number UWAL 2100 Product group 5754 Material XX Hardness XXXX Thickness XXXXXX Width Material conditions H111 / H22 / H24 semi-hard / O soft (other hardnesses upon request) according to DIN 485-2 or
5754 - H22 Sheet and Plate. Aluminium 5754 has excellent corrosion resistance especially to seawater and industrially polluted atmospheres. It has higher strength than 5251. This high strength makes 5754 highly suited to flooring applications. Please note that Mechanical Properties shown are for
Aluminium Blech EN AW-5754 (AlMg3) H22 Mill-finish | Maße online konfigurieren und direkt beslen. Standardbleche einfach im Kloeckner Online-Shop
AW-5754 H22 Gęstość 2.7 [g/cm 3] Moduł sprężystości E 70500 [MPa] Moduł sprężystości poprzecznej G 26500 [MPa] Liczba Poissona 0.33 Temperatura krzepnięcia 595 [°C] Temperatura płynięcia 645 [°C] Ciepło właściwe w 20 °C 897 [J/kgK] 23.7
5754,5754,5754,5754,5754,,、,5754,,5754,,!
Aluminium 5754 / AlMg3 Aluminium 5754 (AlMg3) is een zeewater bestendige aluminium-magnesium legering. De bijzonder goede corrosiebestendigheid zorgt ervoor dat deze legering goed toe te passen is in de maritieme sector. De legering is evenals ongelegeerd aluminium niet termisch hardbaar. Deze legering heeft echter een hogere sterkte ten opzichte van ongelegeerd aluminium. Dit komt
EN AW 5754 is een ‘zeewaterbestendige’ aluminium-magnesium legering met een gemiddelde sterkte. Doordat het materiaal goed corrosiebestendig is, wordt het veel gebruikt in de maritieme sector. Aluminium 5754 bevat 3% magnesium, hierdoor worden hogere mechanische waarden bereikt dan
Der Werkstoff 3.3535, auch bekannt unter der DIN EN AW 5754 bzw. AlMg3, lässt sich der Gruppe der Aluminium-Magnesium-Legierungen zuordnen. Das Material zählt zu den nichtaushärtbaren und dementsprechend naturharten Werkstoffen.Im Zustand H111 kann dieser als durchschnittlich formstabil charakterisiert
Aluminium foil/strips: EN AW-5754 / EN AW-Al Mg3 Material EN AW-5754 / EN AW-Al Mg3 according to DIN EN 573-3:2009-08 Article number UWAL 2100 Product group 5754 Material XX Hardness XXXX Thickness XXXXXX Width Material conditions H111 / H22 / H24 semi-hard / O soft (other hardnesses upon request) according to DIN 485-2 or
5754 - H22 Sheet and Plate. Aluminium 5754 has excellent corrosion resistance especially to seawater and industrially polluted atmospheres. It has higher strength than 5251. This high strength makes 5754 highly suited to flooring applications. Please note that Mechanical Properties shown are for
El Aluminio Aleación Magnesio EN AW 5754 es una aleación de elevada resistencia mecánica, con buena resistencia a la corrosión, comparable a la del aluminio puro en general y mejor aún que la de éste, si de ambiente marino se trata. Se aplica en caldería, bien sea soldada o remachada. Indicada para la fabricación de recipientes a
Aluminium 5754 / AlMg3 Aluminium 5754 (AlMg3) is een zeewater bestendige aluminium-magnesium legering. De bijzonder goede corrosiebestendigheid zorgt ervoor dat deze legering goed toe te passen is in de maritieme sector. De legering is evenals ongelegeerd aluminium niet termisch hardbaar. Deze legering heeft echter een hogere sterkte ten opzichte van ongelegeerd aluminium. Dit komt
5754 (AlMg3, 3.3535, A95754) Aluminum. 5754 aluminum is a 5000-series aluminum alloy: the main alloying addition is magnesium, and it is formulated for primary forming into wrought products. 5754 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN
EN AW-5754 H114 (AlMg3 W19), EN AW-5754 H12/H22 (AlMg3 F22/G22) < Zpět na technické údaje Obecné informace Slitiny hliníku a magnézia nelze stejně jako nelegovaný hliník tepelně vytvrdit.Pokud jde o měkký nelegovaný hliník, je pevnost EN AW-5754 H114 vyšší díky tvrzení směsných krystalů (vytvrzování tuhého roztoku).). Pevnost může být ještě zvýšena tvářením
EN AW-5754 [EN AW-Al Mg3] 3.3535 Geltungsbereich Dieses Datenblatt gilt für warm- und kaltgewalzte Flachprodukte sowie für gezogene und gepresste Langprodukte aus der Aluminium-Magnesium Legierung EN AW-5754. Anwendung Der Werkstoff EN AW-5754 weist hohe Festigkeitswerte unter den naturharten Aluminiumlegierungen auf und
Al arco bajo gas argón; Por resistencia eléctrica Braseado; Estado: 0. H22. APTITUDES TECNOLÓGICAS. SOLDADURA MECANIZACIÓN Estado: H24. Módulo elástico N/mm. 2. ( a temperatura ambiente de 20ºC) HX8 HX9 HX4 HX6 0 HX2 -5754- (ALUMINIO-MAGNESIO 3%) COMPOSICIÓN QUÍMICA PROPIEDADES
Produktinformationen \"Alu Blech EN AW-5754 H22\" Wir liefern direkt aus unserem Vorrat – auf Wunsch auch mit Abnahmeprüfzeugnis. Nutzen Sie die AMCO Datenblätter und informieren Sich über technische, mechanische Eigenschaften, Anwendungsbereiche Lieferformen und
5754 (AlMg3, 3.3535, A95754) Aluminum. 5754 aluminum is a 5000-series aluminum alloy: the main alloying addition is magnesium, and it is formulated for primary forming into wrought products. 5754 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN
Al arco bajo gas argón; Por resistencia eléctrica Braseado; Estado: 0. H22. APTITUDES TECNOLÓGICAS. SOLDADURA MECANIZACIÓN Estado: H24. Módulo elástico N/mm. 2. ( a temperatura ambiente de 20ºC) HX8 HX9 HX4 HX6 0 HX2 -5754- (ALUMINIO-MAGNESIO 3%) COMPOSICIÓN QUÍMICA PROPIEDADES
EN- AW 5754 H111 5754 . ¥ 25.5 0. 2 . . EN- AW 5754 5754 . ¥ 20.4 0. 2 . . EN- AW 5754
H22 G22 EN AW-5754 Kaltverfestigt und rückgeglüht - 1/4 hart T4 F39-40 EN AW-2021A Lösungsgeglüht und kaltausgelagert T451 F39-40 EN AW-2021A Lösungsgeglüht, durch kontrolliertes Recken entspannt (Reckgrad: Bleche 0,5% bis 3%, Platten 1,5% bis 3%, gewalzte oder kalt nachverformte Stangen 1% bis 3%,
Description 5754 (AlMg3, 3.3535, A95754) Aluminium Plates, 5754 H22 Aluminium Plates Supplier, Manufacturer – ASTM B209, ASTM-B-209, EN573, EN485 AA5754 is one of the most widely used aluminium alloys. 5754 aluminum is an alloy of aluminum, further classified within the AA 5000 series (aluminum-magnesium wrought alloy). 5754 is the Aluminum Association (AA) designation for this
aluminium grade 5754 h22 . If you have any questions or good suggestions on our products and site, or if you want to know more information about our products, please write them and send to us, we will contact you within one business